Post-cracking behavior of blocks , prisms , and small concrete walls reinforced with plant fiber

Structural masonry using concrete blocks promotes the rationalization of construction projects, lowering the final cost of a building through the elimination of forms and the reduction of the consumption of reinforcement bars. Moreover, production of a block containing a combination of concrete and vegetable fiber sisal results in a unit with properties such as mechanical strength, stiffness, flexibility, ability to absorb energy, and post-cracking behavior that are comparable to those of a block produced with plain concrete. Herein are reported the results of a study on the post-cracking behavior of blocks, prisms, and small walls reinforced with sisal fibers (lengths of 20 mm and 40 mm) added at volume fractions of 0.5% and 1%. Tests were performed to characterize the fibers and blocks and to determine the compressive strength of the units, prisms, and small walls. The deformation modulus of the elements was calculated and the stress-strain curves were plotted to gain a better understanding of the values obtained. The compression test results for the small walls reinforced with fibers were similar to those of the reference walls and better than the blocks and prisms with added fibers, which had resistances lower than those of the corresponding conventional materials. All elements prepared with the addition of sisal exhibited an increase in the deformation capacity (conferred by the fibers), which was observed in the stress-strain curves. The failure mode of the reference elements was characterized by an abrupt fracture, whereas the reinforced elements underwent ductile breakage. This result was because of the presence of the fibers, which remained attached to the faces of the cracks via adhesion to the cement matrix, thus preventing loss of continuity in the material. Therefore, the cement/plant fiber composites are advantageous in terms of their ductility and ability to resist further damage after cracking.


Introduction
The growing study of new materials with good performance and low cost has led to the use of vegetable fibers as replacements for synthetic fibers that are typically employed as reinforcement in composites.Tropical countries such as Brazil have an abundance and diversity of vegetable crops, and thus a large supply of fibers, enabling their use in construction elements.The overall goal is to improve the physical and mechanical properties of construction materials to be able to build higher performing structures.Several studies have been developed with respect to the fibrous residues from agroindustry, including sisal fibers, banana peels, and the pulp from eucalyptus trees, among others.Noteworthy is the work of Holmer Savastano Jr. [1], who showed that agricultural waste can be used as a raw material for the reinforcement of alternative cementitious matrices and determined that optimal physical performance and adequate structural integrity in manufactured concrete elements could be obtained.Priscilla Pereira [2] evaluated the addition of piaçava fibers to concrete for the manufacture of blocks and prepared a unit with higher tensile strength and optimal conditions for use.Ventura [3] performed bending tests on three different locations in concrete specimens reinforced with sisal fiber, demonstrating that the composite had a greater capacity for deformation than a conventional composite.The aim of Marcelo de Souza Picanço [4] was to study the effect of the addition of curauá fiber, sisal, coir, and jute to cementitious composites with the view of replacing asbestos.The results indicated that the fibers conferred higher ductility and resilience after matrix cracking.The interest in the use of vegetable fibers as reinforcement materials in concrete is linked to their low cost, high availability, and low energy consumption for production.In addition to the economic benefits, vegetable fibers improve the mechanical performance of these materials, such as increasing the tensile strength, controlling the opening and propagation of cracks, and reducing the stiffness of composites, thus making them more ductile and able to undergo greater deformations without loss of integrity (Savastano) [1].

Sisal fiber
Sisal is a plant resistant to dry weather and intense sun exposure and is cultivated in tropical and subtropical regions.It is a common plant in northeastern Brazil, with nearly a million workers directly dependent on this plant for their livelihoods.Currently, Brazil is the largest producer of sisal in the world, and the state of Bahia is responsible for 80% of the nation's fiber production.The sisal is formed into fiber sheets that, after beneficiation, are intended mainly for use in the rope and craft industries for the manufacture of twine, bags, some types of fabrics, reinforcing wire cable, pipes, nets, and carpets.Although the use of the fiber is most popular in the industry manufacturing rope, its value can be increased if used as a reinforcement for composites.Among other advantages, one can point to its abundance in Brazil, ease of cultivation, biodegradability, the fact that it is a renewable resource, and its good properties such as thermal and acoustic insulation.These factors coupled with its high toughness, abrasion resistance, and low cost make sisal one of the most studied natural fibers.
Because of a high incidence of permeable pores, including gaps and lumens, vegetable fibers, including sisal fibers, have a smaller apparent density than their actual density and also a high water absorption (greater than 90%), which affects their adherence to cementitious matrices (Savastano [5]).The loss of ductility in moist and alkaline environment, high water absorption and the heterogeneity of their physical and mechanical properties are the most important factors that adversely affect the performance of vegetable fibers, when applied to reinforcement matrices based on Portland cement.Sisal fibers, despite having characteristics that may negatively affect the reinforcement of Portland cement pastes, also have other favorable attributes that contribute to the good performance of such composites.These positive factors can be better leveraged with the development of improved production techniques and appropriate conservation of these fibers.

Composite materials
A composite is typically formed of two phases: the matrix and the reinforcing element.Matrices consist of agglomerates and mineral aggregates that result in concrete, mortar, or pastes according to the specific application.In simplified form, the reinforcing components impart additional strength by transferring and homogeneously distributing forces throughout the matrix.In addition, the fibers act as obstacles that inhibit the propagation of cracks, leading to progressive ruptures by partially absorbing the energy associated with them, thus ensuring that the capacity of an element is retained (Caetano et al. [6]).Furthermore, parameters such as quantity, relative volume, length, shape, and orientation of the fibers influence the performance of the composite materials.With a higher quantity of fibers, the number of microcracks intercepted by the fibers increases, improving the strength and toughness.The performance of the set improves because the propagation of cracks is slowed and the maximum tension is increased because of the increase in the mechanical strength.The mechanical strength is also enhanced because the load imposed on the matrix is partially transferred to the fibers, which then absorb some of the internal tension.On the other hand, increasing the amount of fiber is intrinsically linked to a reduction in the workability of the mixture due to the absorption of water and the wettability, which can cause consistency problems (Caetano et al. [6]).

Mechanism of rupture in masonry elements
In masonry walls or prisms, forces of all types may occur, such as compression, tensile, bending, and shear forces.The function of the mortar is to uniformly absorb and transmit these forces.Medeiros [7] cites Hilsdorf theory to explain the rupture of typical vertically loaded masonry walls built with blocks seated using lateral completion of the horizontal joints, which occurs through the propagation of vertical cracks in the upper wall thickness.According to this theory, also known as the Tensile Transverse Fracture Mechanism, rupture is caused by the difference in stiffness between the mortar and block.Because of this difference, when the wall is subjected to compression, the deformation of the laterally Post-cracking behavior of blocks, prisms, and small concrete walls reinforced with plant fiber For concrete masonry, the rupture usually occurs because of traction in a block under relatively low compressive stress, and the lateral traction is the dominant strain in the biaxial state.Thus, the function of existing fibers in concrete blocks is of reinforcement.The fibers allow the transfer of tensile forces, decrease crack propagation, control crack opening, and can help delay the rupture of masonry units.Thus, the main objectives of this research were to evaluate the post-cracking behavior of blocks, prisms, and small concrete walls reinforced with sisal fiber through axial compression tests and determination of the deformation modulus.

Materials and experimental program
The composites were produced using sisal fibers provided by Sisal Weaving (Tecsal, State of Bahia, Brazil).These Type 3 sisal fibers are used to make general yarns and Bale Twine, a type of agricultural yarn, for export.Sisal fibers with lengths of 20 mm and 40 mm were incorporated at volumetric fractions of 0.5% and 1% in concrete.The density, water absorption, and moisture content of the fibers were determined.Blocks of concrete with and without fibers were manufactured with a characteristic strength of 4 MPa at Tatu Precast (Limeira, São Paulo, Brazil).Five series were produced in total, with the first series as a reference.The remaining series were differentiated by the added fiber content compared to the volume of concrete and length of the fibers.Table 1 presents the nomenclature for the building blocks in each series.Axial compression tests were performed on the blocks, prisms, and small walls constructed using the concrete with and without added fibers according to NBR 12118: 2007 [9] for the blocks, NBR 8215: 1983 [10] for the prisms, and NBR 8949: 1985 [11] for the small walls.The equipment used for the tests belonged to the Structures Laboratory of the School of Engineering of São Carlos (EESC) at the University of São Paulo (USP).A total of 90 blocks (18 per series), 60 prisms, (12 per series), and 15 walls (three per series) were tested.The modulus of deformation was calculated for the prisms and small walls in accordance with the requirements of the ACI 530-92 standard [12].According to this standard, the modulus is given by the slope of the secant line on the stress-strain diagram between 5% and 33% of the rupture strain.A linear variable differential transformer (LVDT) was used for the measurements.Two displacement transducers were confined mortar causes transverse tension in the blocks (Figure 1).According to Solórzano [8], authors such as Lenczner (1972), Sutherland (1981), and Sinha & Hendry (1987) show full agreement that bi-and triaxial stresses produced in masonry are subjected to compressive stress.These forces occur because of the different deformation moduli of the materials used for the construction of the prisms and walls.According to the abovementioned theory, the mortar is less rigid than the blocks; i.e., it has a greater deformation under load and tends to be expelled.Accordingly, the deformation induced in a mortar produces lateral tensions tangential to the plane of the joint that are restricted by the masonry units.These are thus subjected to traction lateral stresses that cause rupture through the development of cracks parallel to the axis of loading.Figure 2 shows the state of the triaxial compression stress in the mortar and the lateral axial traction in the blocks.
blocks were air dried and tested using power control at a constant speed of 2.03 kN/sec.The prisms and small walls were tested in a servo-controlled IN-STRON 8506 instrument with System 5000 for data acquisition (Figure 6).These elements were tested with displacement control and a constant speed of 0.005 mm/s.A 35-mm-thick steel plate and a steel profile were placed on the tops of the prisms and small walls, respectively, to generate the uniform distribution of the load.Only one type of mortar was used for the fabrication of the prisms and small walls.The mortar was a mixture of cement, lime, and sand, and is the most suitable for use in masonry structures.The British Standard BS 5628: Part 1: 1992 [13] prescribes traces for medium used for the prisms and four for the small walls to create a maximum measurement field for a displacement of 20 mm and a resolution of 0.001 mm.The speed of the enforcement displacement was 0.005 mm/s, and the measurements were recorded every 1.5 s using the SYSTEM 5000 data acquisition and storage system.Figures 3 and 4 contain the illustrations of the instrument and locations of the displacement transducers on the prisms and small walls, respectively.Testing of the compressive strength of the blocks was achieved using an ELE brand Autotest 2000 press with a capacity of 2000 kN that was equipped with two supporting plates (Figure 5).The Post-cracking behavior of blocks, prisms, and small concrete walls reinforced with plant fiber and low resistance.A medium resistance mortar was chosen with a trace volume of 1:0.5:4.5 for cement, lime, and sand, respectively.
For a better understanding of the results and to obtain satisfactory conclusions, a statistical analysis of the influence of fiber addition on the compressive strength of the blocks, prisms, and small walls was also conducted using the program OriginPro 7.5.

Block manufacturing process
The materials used to manufacture the blocks were CPV ARI PLUS cement, gravel, stone powder, and sand.In compliance with the company's environmental policy, a recycled aggregate was used as a replacement for 30% of the natural aggregates.The recycled aggregate originated from recyclable elements rejected by quality control, the remains of fresh concrete, and units damaged during transport and storage (Figure 7).The blocks were produced on an industrial scale in the TATU factory and were precast using the same trace for each type of unit in which all inputs-with the exception of the cement and fibers-were measured in volume.The sisal fibers and cement were weighed separately and placed directly into the mixer.Adjustment of the water content of the trace for each series of blocks was performed on the basis of a visual evaluation by the molding operator.The blocks were produced in a Piorotti BLOCOPAC 1300 vibropress for different production times.The use of this type of equipment allows for the production of units with high strength, good workmanship, low cement consumption, and good compaction of the concrete.The order of presentation of the materials followed the appropriate sequence for the equipment used.Initially, the amount of all aggregates was determined.After the introduction of the cement and fibers (for the blocks containing fibers), the material was mixed for about 1 min.Water and additives were then added, and the final blend was mixed for approximately 3 min.The molding of the blocks was achieved by adjusting the feeding times, vibration, agitation, and demolding of the vibro-press.In defining these times, the experience of the molding operator was essential.After completion of the pressing, the freshly molded blocks were transferred to cure chambers.Thermal curing was achieved overnight and consisted of a cycle lasting 4-5 h at a constant temperature of 60° C.

Results and discussion
The results are presented with their respective analyses.The values are displayed in tables that include the mean, standard devia-tion (Sd), and coefficient of variation (CV) for each of the samples.Statistical tests included an analysis of variance (ANOVA) test with one factor and an ANOVA with two factors.The first test indicated that if there were any statistically significant differences between the compressive strength of the blocks, prisms, and small walls as a result of the small addition of fibers.On the other hand, the second test indicated if the length and volume content of the fibers influenced the compressive strength of the blocks, prisms, and small walls.Post-cracking behavior of blocks, prisms, and small concrete walls reinforced with plant fiber Savastano [1] obtained apparent density values of sisal fiber between 400 and 500 kg/m3, which are lower than those obtained for the fibers used in this study.The values for the maximum water absorption over 24 h were also lower than those reported by Toledo Filho [14] and Savastano [1] (193% and 151%, respectively).The results of the density for both saturated and air-dried blocks with and without the added fibers are presented in Table 3.The values for the blocks containing the sisal fibers are smaller than those for the blocks without fibers.This difference results because the fibers and voids introduced by them act as air-entrainment agents.

Compressive strength of the blocks
Table 4 shows the average and characteristic compressive strengths, (f bm ) and (f bk ), respectively, of the blocks.The testing was performed 28 days after the blocks and elements were made.
As can be seen from the results of the compression tests, the blocks containing sisal fibers showed an average decrease of 41% in resistance compared with that of the reference blocks.The ANOVA performed on these results indicated that the average values for the reference and fiber-containing samples were different.In particular, the compressive strength of the blocks without the added fibers was significantly higher than that of the blocks with the added fibers at a 95% confidence level.This result can be linked to the lower densities of the blocks containing the fibers.It is also likely that other factors contributed to the strength reduction, such as weak interactions between the fibers and cement matrix, causing damage to the structure of the material.In addition, it was difficult to mold, press, and compact the dry concrete containing the added sisal, which may have led to the formation of defects in the blocks.
With respect to the characteristic strength, all blocks met the criteria for the 4-MPa class, which had been requested by the manufacturer.In Table 4, it can be observed that the blocks with 20-mm-long fibers had a higher resistance than the blocks with 40-mm-long fibers.This result may be related to the fact that the smaller fibers were better accommodated and distributed in the relatively small blocks compared with the larger fibers.On the basis of the ANOVA test with two factors, it was concluded that the length influenced the compressive strength of the reinforced blocks; the units containing 20-mm-long fibers exhibited a higher resistance compared with the units containing 40-mm-long fibers for a given fiber content at a significance level of 0.05.Finally, the resistance of the blocks with a fiber content of 0.5% and 1% were similar for both fiber lengths.The resistance of the blocks with 1% fiber content was slightly greater than that for the blocks containing 0.5% fibers.However, the two-way ANOVA test    showed that there was no statistical difference in the average values for the compressive strength of the blocks with 0.5% and 1% added fiber.

Compressive strength of the prisms
The values for the compressive strength of the prisms correspond to the gross area (f p ) and are presented in Table 5.According to the statistical analysis, there were significant differences between the means of the five samples.In particular, the compressive strength of the prisms without the added fibers was greater than that of the prisms containing fibers at a confidence level of 95%.In fact, the prisms reinforced with fibers showed an average decrease of 28% in resistance compared with the resistance of the prisms without any fibers.Furthermore, the prisms with 20-mm-long sisal fibers showed better performance and greater resistance than the prisms with 40-mm-long fibers at a given fiber content.The two-way ANO-VA test showed that the fiber length influenced the compressive strength of the reinforced prisms.Thus, the prisms containing 20-mm-long fibers exhibited higher strength than the prisms containing 40-mm long fibers 40 mm fibers for the same fiber content at a significance level of 0.05.With respect to the volume fraction of fibers, the prisms with 1% added sisal fibers of the same length exhibited higher performance.This factor was more significant in prisms than in blocks, and thus, the fibers contributed more to the bearing capacity of the element.As a result, the fiber content actually influenced the compressive strength of the prisms.

Compressive strength of the small walls
The results of the tests on the compressive strength of the small walls in relation to the gross area (f pp ) are shown in Table 6.Note that no significant change in the compressive strength of the small walls was observed when blocks containing sisal fibers were used, and the values very close to or even higher than those obtained for the smaller walls constructed with blocks that did not contain any fibers were obtained.In fact, the elements consisting of blocks with 1% added 20-mm-long fibers had a higher resistance than the walls constructed of blocks without the added fibers.In addition, according to the ANOVA test, the means of the samples were similar at a significance level of 0.05.This result may be associated with the mechanical behavior of the blocks and elements, which differs for each type of component and element tested.Larger tensile stresses appear in the walls mainly because of the lagged vertical joints.Under this type of stress, the fibers act as efficient reinforcement.The horizontal tensile stresses were lower in the prisms than in the walls because they were generated solely due to the difference in the rigidity of the blocks and mortar.Moreover, in the prisms, and particularly in the blocks, the compression test is always characterized by a certain confinement effect that contributes to a reduction in the tensile stresses in the units.The ANOVA test revealed that neither the length nor the fiber content significantly influenced the compressive strength.Thus, it can be concluded that the increase in the compressive strength of the elements with added 20-mm-long fibers was not statistically significant in comparison with the fiber elements containing 40-mm-long fibers for a given fiber content.The same conclusion can be drawn   Post-cracking behavior of blocks, prisms, and small concrete walls reinforced with plant fiber  for the increase in the compressive strength with the added fiber content from 0.5% to 1.0% for fibers of the same length.

Deformation modulus and stress-strain curves for the prisms and small walls
The deformation modulus was calculated for the prisms and small walls in accordance with the requirements of ACI 530-92 [12].According to this standard, the modulus is given by the inclination of the secant line in the stress-strain curve between 5% and 33% of the breaking strain.
The results for the modulus of deformation of the prisms (E p ) are presented in Table 7. Notably, both strain and modulus refer to the gross area of the elements.The Def. 33% column shows the deformation at 33% of the breaking strain, and the Def.Last column indicates the deformation at the moment of breakage.The rigidity of the prisms containing the added fibers was lower than that of the prisms without the fibers.The deformation modulus of the prisms with the added fibers underwent an average reduction of 28% compared with the values for the prisms that did not contain any fibers.In the study conducted by Picanço [4], the same tendency was observed in composites with added vegetable fibers The stress-strain curves were drawn and organized by type of prism in Figure 8.According to the diagrams, there is variation in the results, and thus, it impossible to determine the deformability and effect of the pres- Post-cracking behavior of blocks, prisms, and small concrete walls reinforced with plant fiber ence of the fibers in the blocks.This variation may be associated with the loading and unloading cycles, which were only performed up to 10% of the failure load expected for the prisms.It is probable that the execution of the cycles up to 30% of the ultimate load would lead to a reduction in the variability and enable analysis of the data.
In the PR20-1% graph, it can be observed that stress concentration occurred at one side of the prism, causing crushing and tensile stresses in the meter positioned on the opposite side.This result can be verified by the tie formed in the stress-strain curve near the rupture.
Although the stress-strain curves of the prisms could not be used to better visualize the results, note that most reinforced elements showed extension of the post-peak curves.Thus, it can be said that there was a gain in capacity for the absorption of deformation and that the addition of the fibers was advantageous with respect to im- Table 8 shows the results for the modulus of deformation for the small walls (E pp ).There was a small decrease in the rigidity of the walls with the addition of fibers to the blocks compared with that of the walls constructed with blocks that did not contain fibers.This reduction was equal to approximately 12%, considering the overall average.The stress-strain curves for the small walls are arranged in Figure 9 according to each sample type.No marked difference was observed in the compressive strength of the walls for different samples.Thus, it can be clearly noted that the addition of sisal fibers to the blocks used to construct these elements contributed to a gain in the deformation capacity.According to Savastano [1], cracks begin to form at the time of composite failure, but their growth is constrained by the presence of fibers.When the cracks begin to join, the sum of their effects influences the toughness of the element due to large deformation of the material.In this case, there is an explanation for the increased toughness afforded by the addition of fibers because they are responsible for incorporation of voids and discontinuities; these fibers can absorb an increased amount of energy during cracking while at the same time limiting the spread of the cracks.

Rupture type for the elements
It was observed during the compression tests that an instant collapse occurred in the nonreinforced units (Figure 10).In contrast, the blocks reinforced with sisal fibers did not undergo a brittle fracture, as shown in Figure 11.The same behavior was observed for the prisms.The elements with  added sisal fibers experienced a ductile rupture, with the fragments remaining linked by the fibers due to their adhesion to the matrix (Figure 12).However, a sudden rupture occurred in the elements without fibers, which is characteristic of brittle behavior (Figure 13).The parts of the reinforced elements, even after they were broken, were held together by the fibers, and thus, the elements did not lose their continuity and the breaks were progressive.According to Campos [15], this behavior indicates that the fibers were capable of joining the faces of the cracks.As a result, they imparted a certain load capacity after cracking, although small, that contributed to an increase in the toughness of the elements containing them.Another advantage of using the fibers as a reinforcement material in concrete is delayed cracking, which leads to improved system performance.Table 9 shows the first cracking load and its relationship to the ultimate strength of the small walls.As observed, the first cracking load of the walls containing the fibers occurred at a higher percentage relative to the final strain, and there was a delay in the cracking of these elements.

Cracking of the prisms and small walls
In the prisms, in most cases, vertical cracks developed along the lateral septa.The cracks were initiated near the mortar joints and Figura 14 -Typical break of the prisms under compression Post-cracking behavior of blocks, prisms, and small concrete walls reinforced with plant fiber spread throughout the height of the element, with breakage by traction in the region near the joint.Figure 14 shows the typical crack formation for each type of prism.According to Mohammed [16], because the mortar is less rigid than the blocks, which is true in most cases, there is a tendency for the mortar to deform more than the units.However, this deformation is prevented by the adherence to the other components, which gives rise to tensile stresses in the units transverse to the vertical axis of compression.With respect to cracking of the walls, vertical tensile cracks were observed that started at the vertical joints and progressed to the cutting blocks, leading to their rupture (Figure 15).The appearance of this type of cracking can be explained by the presence of vertical joints in these elements.In general, there were vertical cracks along the lateral septa, with breakage occurring because of transverse traction in the blocks, as illustrated in Figure 16.In most of the small walls without fibers and also in some of the small walls with the added fibers, crushing occurred between the horizontal and vertical joints (Figure 17).

Conclusions
n According to statistical studies, blocks containing fibers experienced a decrease of 41% in the average compressive strength compared with that of the reference blocks because of flaws in the material structure, although they exhibited the desired level of resistance.The reinforced prisms showed better performance than the reinforced blocks with an average decrease of 28% in strength compared with the reference prisms.In turn, the small walls with sisal fibers had a mean reduction of just 3% in the resistance compared with that of the standard elements.
n The small walls best represent the typical failure mode in masonry, in which larger tensile stresses appear in the units because of the lagged vertical joints.Under this type of stress, the n Because sisal has a low deformation modulus, its functions mainly after matrix cracking.It enables greater energy absorption and imparts some ability to absorb loads after cracking, which helps to increase the toughness and ductility of the material.
n The failure mode was well characterized in all sample types tested.The units and elements with added fibers always underwent ductile rupture.However, sudden rupture occurred in the elements without fibers, which is characteristic of fragile behavior.Thus, the fibers united the faces of the cracks because of adhesion with the cement matrix and prevented loss of continuity of the material.

Figure 3 -
Figure 3 -Front and plan view of the location displacement transducers prisms

Figure 5 -
Figure 5 -Test of resistance to compression of the blocks

Figure 7 -
Figure 7 -Aggregates used to manufacture the blocks

Figure 8 -
Figure 8 -Stress-strain curves of each type of prisms

Figure 9 -
Figure 9 -Stress-strain curves of each type of small walls

Figure 10 -
Figure 10 -Fragile break of the blocks without the added fiber

Figure 11 -Figure 12 -
Figure 11 -Ductile break for the blocks with the added fiber

Figure 13 -
Figure 13 -Fragile break of the prisms without the added fiber

Figure 17 -
Figure 17 -Crushing of the mortar

Table 1 -
Type series of blocks manufactured

Table 2
lists the physical properties of the fibers.The low apparent density and high water absorption are common characteristics of vegetable fibers because of the large number of permeable pores, including gaps and lumens.

Table 2 -
Physical characterization of sisal fiber

Table 3 -
Specific density of the blocks with and without fiber

Table 4 -
Compressive strength of the blocks

Table 5 -
Compressive strength of prisms with and without fiber addition

Table 6 -
Compressive strength of small walls with and without fiber addition

Table 7 -
Module deformation of the prisms with or without addition of fiber

Table 8 -
Deformation modulus of the small walls with and without fiber addition

Table 9 -
First cracking load and breaking load of small walls