Influence of reinforcement ’ s corrosion into hyperstatic reinforced concrete beams : a probabilistic failure scenarios analysis

Resumo This work aims to study the mechanical effects of reinforcement’s corrosion in hyperstatic reinforced concrete beams. The focus is the probabilistic determination of individual failure scenarios change as well as global failure change along time. The limit state functions assumed describe analytically bending and shear resistance of reinforced concrete rectangular cross sections as a function of steel and concrete resistance and section dimensions. It was incorporated empirical laws that penalize the steel yield stress and the reinforcement’s area along time in addition to Fick’s law, which models the chloride penetration into concrete pores. The reliability theory was applied based on Monte Carlo simulation method, which assesses each individual probability of failure. The probability of global structural failure was determined based in the concept of failure tree. The results of a hyperstatic reinforced concrete beam showed that reinforcements corrosion make change into the failure scenarios modes. Therefore, unimportant failure modes in design phase become important after corrosion start.

Influence of reinforcement's corrosion into hyperstatic reinforced concrete beams: a probabilistic failure scenarios analysis

Introduction
Reinforced concrete is one of the most used types of construction material around world.There are several advantages on using this type of solution such as its relative low production cost, facility to obtain its components, adaptability to complex geometries, high strength capacity and chemical properties [1].The mechanical properties such as strength and stiffness have major importance in the context of reinforced concrete design as it is related to the resistance limit state.However, the interest on structural durability had a considerable advance in the last few years due to the large cost associated to structure repair and maintenance.NBR 6118 [2] prescribes rigorous design criteria in order to ensure durability in reinforced concrete structures.To improve the durability of reinforced concrete structures, engineers have to design taking into account the water/cement ratio adopted into concrete mixture, concrete cracking control, the environment aggressiveness and the prescribed cover depth.However, design codes do not present further recommendations aiming the structural durability analysis.It provides only guidelines that should be considered without information concerning the assessment of durability problems, which justifies the development of the present research.Among the processes that reduce the durability of reinforced concrete structures, reinforcement's corrosion is mentioned as the major cause.The corrosion process produces the concrete cracking, cover spalling, loss of steel rebar cross section and yield stress and, consequently, the decrease of the mechanical strength along time.The corrosion process may derive from carbonation and/or high content of chloride ions, for instance, [3][4][5].However, among such processes, the chloride penetration is the most important process that triggers the reinforcements corrosion [6].Therefore, the modelling of chloride penetration and reinforcements corrosion lead to the accurate assessment of reinforced concrete durability.The rebar corrosion phenomenon in reinforced concrete structures due to chloride penetration starts when the chloride concentration at the rebar/concrete interface reaches a threshold value.At this moment, the amount of hydroxyl into concrete pores exceeds the chemical threshold, causing the depassivation of the chemical layer protection around the steel rebar [7].The chloride concentration at reinforcements interface grows along time and reaches the threshold value due to the ions transport from the external structural surface into it.The chloride ingress into concrete pores is a complex phenomenon governed by complex physical and chemical mechanisms.However, the representation of this phenomenon may be simplified considering only the chloride ions diffusion along the concrete cover.In this context, several models have been proposed in literature.Among them, it is worth to mention [8], which presents mathematical models to represent the particles movement in saturated concrete.Samson and Marchand [9] studied the influence of temperature on the chloride transport into concrete pores.Bastidas-Arteaga et al. [10] presented a study on the mechanical degradation processes caused by reinforcement's corrosion, concrete cracking and bio deterioration, as well as their combined influence on the strength reduction of reinforced concrete elements along time.Zhao et al. [11] analysed the mechanical degradation on the concrete cover from corrosion processes in non-cracked stages, initially, and then in partially cracked stages.In spite of many proposed models in literature, such models deals the reinforcement's corrosion considering deterministic approach-es, i.e., the influence of the inherent randomness is not accounted.As the corrosion involves chemical, mechanical and environmental parameters, which are uncertain, the randomness influence is widely significant.Therefore, this mechanical problem is represented consistently and realistically when the randomness is properly addressed.As a result, deterministic variables become probabilistic and uncertainties are accounted.There are studies in literature using simple mathematical models to represent the chloride diffusion phenomenon into concrete pores combined with statistical approaches to model the uncertainties influence on the prediction of structural safety along time.Frangopol et al. [12], for instance, proposed a model to represent the mechanical behaviour of reinforced concrete girders as a function of time.In this model, the Fick's law was applied to represent the chloride diffusion process along time, empirical laws were adopted for the quantification of reinforcement's cross section loss and the Monte Carlo simulation method was used to carried out the probabilistic analysis.Nogueira et al. [13] performed a study on the determination of corrosion start using a probabilistic approach by the coupling between Fick's law and reliability theory.In this work, the influence of uncertainties associated with concrete cover depth and water-cement ratio on the probability of structural life failure was analysed.Nogueira and Leonel [14] proposed a simplified method to determinate the optimal maintenance time as a function of water-cement ratio, cover depth and environment aggressiveness.Interaction abacuses were proposed in order to determine optimum values of concrete cover according to maintenance time fixed a priori.Liberati et al. [15] proposed the coupling among Fick's law, reliability algorithms and damage mechanics to predict the structural life based on a robust finite element code.Such model allowed the elastoplastic behaviour of reinforcements and quasi-brittle behaviour of concrete.In spite of several studies presented in literature concerning reinforcement corrosion modelling, aggressive mechanisms and chloride transport modelling, few studies have been observed focusing in the influence of corrosion on the global mechanical behaviour of reinforced concrete elements along time.Especially in the context of hyperstatic structures where effort distribution must be accounted.Normally, bending failure tends to be ductile whereas shear failure exhibits brittle behaviour in reinforced concrete structures.Therefore, brittle failures must be avoided and ductile failures must be predicted in design.However, change on the structural failure mode may occur due to reinforcements corrosion effects.Ductile failure, initially predicted in design, may not be the major weak structural link after corrosion start.As reinforcements area is lost during corrosion, effort distribution is observed and failure configurations different from those predicted in design may appear.In such context, the present research aims to study the influence of reinforcement's corrosion phenomenon on the mechanical strength of hyperstatic reinforced concrete beams.One goal of this study concerns the determination of structural failure scenarios change along time.The mechanical modelling of corroded reinforced concrete structures is performed by coupling Fick's law, for chloride diffusion representation, to analytical approaches based on [2], to predict bending and shear structural resistance along time.The reduction on the reinforcements area and yield stress due to corrosion is modelled by empirical approaches.In addition to that, reliability theory is coupled to mechanical model in order to consider the inherent uncertainty on the physical problem.The

G. P. PELLIZZER | E. D. LEONEL | C. G. NOGUEIRA
Monte Carlo simulation method is applied to assess the probability of each individual failure mode.The probability of global structural failure is achieved based in the concept of failure tree.Consequently, the applied model performs mechanical analyses in the probabilistic domain.A hyperstatic beam is analysed in this study and the change on the failure modes, individual and global, according to the corrosion evolution is represented, which is the main contribution of this work.Moreover, the evolution of the probability of failure, for global and each individual failure mode, is assessed, which is another contribution of this study.

Simple bending and shear strengths
The evaluation of strength in reinforced concrete members considering simple bending and shear cases is performed based on classical hypothesis and models described by the Brazilian standard [2].Figure 1 illustrates the cross section of a rectangular beam subjected to bending moment M, containing width b w , height h, effective depth d, tensile steel area A s , compression steel area A s ' , neutral axis position x and strength of compression concrete f ck .The neutral axis is defined by the distance x, which value is null at the cross-section end, at is more compressive fibre.By adopting the simplification of plastic depth allowed by the parabolic-rectangle diagram for compression concrete, given by y = 0.8x, and enforcing the cross section equilibrium the bending design moment and neutral axis position are obtained.In such equilibrium condition, the external bending moment is equilibrated by the resistant bending moment, which is due to reinforcements and concrete.By performing the equilibrium in terms of bending moment, the following equation is obtained: (1) ( ) in which M d is the external bending moment applied into the crosssection, normally denominated as bending design moment.
The neutral axis position is determined from Equation 1. Solving such equation for x variable one obtains: (2) After the design of the reinforced concrete element, in which the tensile steel area is determined, the associated resistant bending moment, M resist , is calculated by equilibrium conditions.Such equilibrium results in: (3) ( ) in which: f sk is the yield steel for longitudinal reinforcements.
The determination of shear strength in reinforced concrete structures assumes as valid the hypothesis of generalized truss.It assumes stirrups positioned at 90º with the beam axis and spaced at each s.In addition to that, the shear resistance is determined considering the values of transversal reinforcement area A sw , concrete compressive characteristic strength f ck (MPa), steel yield for transversal reinforcement f yw (MPa), b w and d given in metre.
The shear resistance of a rectangular cross section, V resist (kN), belonging to a reinforced concrete beam is calculated by [16], considering the parameters described in the present paragraph, as follows: (4) Figure 1 -Rectangular cross-section of a rectangular reinforced concrete beam.Hypothesis, stress and strain distributions for failure limit state

Influence of reinforcement's corrosion into hyperstatic reinforced concrete beams: a probabilistic failure scenarios analysis
It is important to mention that during the durability analysis, in which steel reinforcements area is lost along time, the neutral axis position, Equation 2, is updated at each time step.Therefore, as the reinforcements are corroded the neutral axis is recalculated.
Another important remark that must be mentioned concerns the safety coefficients for design.The hyperstatic beam analysed in this study was designed considering safety coefficients.Then, the steel reinforcements areas were determined considering safety coefficients on the concrete and steel strengths and on the loading actions.Nevertheless, the probabilistic analyses were carried out disregarding such safety coefficients.Therefore, the characteristic values for all variables were considered during the probabilistic analyses.

Fick's law
Reinforcement's corrosion due to chloride ingress occurs in the presence of oxygen.Such process stars when the chloride concentration at the rebar contours exceeds a threshold level causing depassivation.Even for well-constructed and controlled reinforced concrete structures, a gradual ingress of chloride content from the external surface into concrete pores may occur according to the environmental conditions of aggressiveness.The transport mechanisms responsible for chlorides movement into concrete are capillary absorption, permeability under pressure, ion migration and ionic diffusion [4].Among them, the most significant contribution is attributed to the ionic diffusion.Therefore, the proposed models, in literature, to represent such phenomenon are based, normally, only into ionic diffusion.Fick's law [17] is an approach that has been widely used to simulate chloride penetration and its transport through concrete pores [7,14,15,18,19,20].It is important to mention that Fick's laws for diffusion assumes the media in which the flow occurs as homogeneous, isotropic and chemically inert.In addition to that, the chloride flow is assumed to be identical along all directions and constant along time.Considering concrete, these hypotheses are not completely satisfied, because concrete is well known as heterogeneous, anisotropic and chemically reactive (continued hydration and micro-cracking process) material.However, the methods commonly adopted for chlorides transportation modelling in concrete consider this process governed only by ionic diffusion.Then, it assumes that the concrete cover is completely saturated.Therefore, it makes the hypotheses of Fick's laws acceptable for the chloride ingress modelling, because, in this case, the material is assumed completely saturated, with unidirectional chloride flux, i.e., from the exterior surface into the concrete depth.When chloride diffuses into concrete, a change in chloride concentration, C, occurs at any time, t, in every point, y, of the concrete, i.e., it is a non-steady state of diffusion.To simplify its analysis, the diffusion problem is considered as one-dimensional.Many engineering problems of chloride ingress, as those discussed in this study, can be solved considering this simplification.For a semi-infinite domain with an uniform fluid concentration at the external surface, the second Fick's law can be written as follows [13-15, 17]: (5) In which: C(y,t) is the chloride concentration at a given depth y and at a time t; C 0 is the chloride concentration at the external surface assumed constant in time; erfc is the complementary Gauss error function; D 0 is the material diffusion coefficient considered constant along time.
From Equation 5, assuming that y is the concrete cover thickness and C(y,t) the chloride concentration threshold, required to eliminate the chemical protective layer of reinforcements, it is possible to determine the time for corrosion start t r as follows: (6) During the corrosion process caused by chloride diffusion, two different phases are observed.The first one, called initiation period, is defined from the construction until the rebar depassivation.The second phase, denominated propagation period, involves the end of initiation period until the structural collapse.The boundary between these two phases is the point characterized by the time of corrosion starts, which is evaluated by Equation 6 [14,15].

Steel area reduction as a function of time
After the start of reinforcement corrosion, the rebar cross-section area reduces until its complete deterioration defining the propagation period.In literature, there are few mathematical models to represent such period as most researches consider as structural life only the initiation period.However, the propagation period can be modelled by empirical equations based on Faraday's laws.According to this approach, the reduction on the rebar cross-section area along time, assuming uniform corrosion process, is determined by the following equation [7,21]: In which: d(t) and d initial are the rebar diameter given in millimetres for actual and initial configurations, respectively; i corr is the corrosion ratio given in µA/cm²; t r is the time for corrosion initiation given in years and calculated according to Equation 6; t is the diffusion time, given in years.Different parameters have influence on the intensity of corrosion or into its rate.Among them, the water-cement ratio w/c and the cover depth y have to be mentioned.In order to account the influence of such parameters, the corrosion ratio is expressed according to [22] as follows: (8)

Steel yield strength reduction as a function of time
In addition to the rebar cross-section area reduction during propagation period, the yield stress of reinforcements is also reduced  [23] performed an experimental study aiming to determine the mechanical residual strength of corroded steel rebar located into reinforced concrete elements.The researchers observed that the decrease on the yield stress occurs faster than the reduction of rebar diameter.According to [23], the reduction of the steel yield stress along time can be evaluated based on the following empirical expression: (9) in which: f y,t e f y,0 are the yield stress for corroded and non-corroded steel rebar at a given time, respectively; Q corr is the amount of reinforcements corrosion given as a percentage of material mass loss.The amount of corrosion is calculated, according [23], as follows: (10) In which: i corr is given in µA/cm² and calculated by Equation 8; the diameter is provided in millimetres and the times in years.

General Concepts
The reliability analysis aims at calculating the probability of failure regarding a specific failure scenario, known as limit state.It is worth to note that reliability R and probability of failure Pf are complementary concepts, in which R=1-Pf.The first step in the reliability assessment is to identify the basic set of random variables for which uncertainties have to be considered.For all these variables, probability distributions are attributed to model its randomness.These probability distributions may be defined by physical observations, statistical studies, laboratory analysis and expert opinion.The number of random variables is an important parameter to determine the computing time consumed during the reliability analysis.To reduce the size of the random variable space, it is strongly recommended to consider as deterministic all variables whose uncertainties lead to minor effects on the value of the probability of failure.The second step consists in defining a number of potentially critical failure modes.For each of them, a limit state function ( ) separates the space into two regions: the safe domain, where ( ) 0 G X > and the failure domain, where ( ) 0 G X < .The boundary between these two domains is defined by ( ) 0 G X = , known as the limit state itself.The probability of failure is evaluated by integrating, over the failure domain, the joint density function, [21]: (11) In which , , , is the joint density function of the variables X.As the evaluation of the above integration is impossible in practice, as the joint density function has not an explicit form, alternative procedures have been developed on the basis of the concept of reliability index, β, or simulation methods [24,25].
In the present study, the Monte Carlo simulation method was applied to evaluate the probability of structural failure for each individual failure mode.Such approach will be presented in the following section.

Monte Carlo simulation
Monte Carlo method is a numerical simulation procedure widely used in reliability problems.In this method, a sampling of random variables is used to construct a set of values aiming to describe the failure and safe spaces in order to calculate Eq. ( 11).The sampling is constructed based on the statistical distribution assigned for each random variable considered in the problem.As this method deals with simulation of the limit state function, as bigger be the sampling adopted more accurate will be the spaces' description and more accurate will be the probability of failure achieved.The kernel of this method consists on the construction of a sampling for the random variables involved in the problem, as described in Figure 2. Figure 2 presents a general sampling scheme assuming two random variables and two limit state functions.The simulation leads to the structural failure when the considered point is located at the failure domain.Otherwise, safety condition is observed.Series schemes consider failure if at least one limit state function be violated.On the other hand, parallel schemes assume failure condition when a set of critical limit state functions are violated.Such set of limit state functions are defined according to the structural system analysed and the failure paths available.In spite of simulation methods be applicable for reliability analysis, optimization approaches such as First Order Reliability Methods (FORM) and Second Order Reliability Methods (SORM) are also available.FORM and SORM are based on the determination of the reliability index, which is associated to the probability of failure.The probability of failure is calculated, for Monte Carlo simulation, using the following equation: (12) The function ( ) i x I can be estimated as follows: (13) By simulating the limit state function for a convenient range of sampling, the mean value of ( ) i x I will be an estimator for the probability of failure.Therefore: Influence of reinforcement's corrosion into hyperstatic reinforced concrete beams: a probabilistic failure scenarios analysis (14) The disadvantage of this method is related to the high number of simulations required to compute accurately the probability of failure.Normally, in order to estimate accurately the probability of failure of 10 n − , the number of simulations must be higher than 10 − , it is required 5 10 to 9 10 real- izations of the limit state function.When complex numerical mechanical models are involved, which lead to high computational time, this method may be not reliable.However, theoretically, when the number of simulations tends to infinity, the probability of failure calculated tends to its real value.Other details about Monte Carlo simulation can be found in [24][25][26][27].

Structure definition
The presented methodology was applied to the probabilistic analysis of a hyperstatic beam.Such beam is supported into three points, and the external load is composed by an uniform distributed load.Figure 3 illustrates the static scheme of the beam.The bending moment and shear effort diagrams are also presented.The reliability analyses were carried out considering the critical efforts presented in Figure 3.The intensity of such efforts is defined as follows: (15) The analysed beam was designed, i.e. the reinforcements areas were determined, assuming a cross section of 20 cm x 40 cm (width x high); permanent load g = 3 kN/m; accidental load q = 20 kN/m; f ck = 30 MPa; f yk = 500 MPa; concrete Young's modulus E c = 26071 MPa.The design procedure recommended by [2] was followed.In addition to that, the following parameters were considered for durability analysis: environmental aggressiveness class III (industrial type with high risk of structure deterioration [2]); concrete cover thickness 4 cm.It is important to stress that the structural design considered safety factors.However, the probabilistic analyses were carried out disregarding all safety factors on the load and material properties.After such considerations, the structure was designed and detailed as shown in Figure 4.
It is worth to mention that in this study serviceability limit states were not accounted.

Safety Evaluation. Mixed model considered and effort redistribution
The reliability theory describes hyperstatic structural systems as redundant systems.Such description appears since the system failure, in this case, occurs after the failure of a number of individual modes equal to the structural hyperstatic degree.Consequently, as more than one limit state must be violated to the global failure be observed, such systems are subjected to load distribution, ensuring higher safety level when compared to simple isostatic schemes.
Considering the studied beam, the global collapse occurs after the consecutive failure of at least two individual failure modes.The failure is assumed when the effort due to the external load, Equation 15, exceeds the structural mechanical capacity given by Equations 3 and 4, in a given cross-section.
It is important to mention that hyperstatic structures presents more than one failure path, i.e. due to the load distribution and the combination of different random variables, the global failure can occur according to different sequences of individual failure modes.
In such cases, the reliability theory based on system approach aims to determine the probability of each individual failure mode as well as the probability of global structural failure.As a result, this approach predict the most probable failure path and the most probable mechanical mechanism of failure.
In order to apply the reliability theory based on system approach it Then, the occurrence of such individual failure mode leads to the mechanical collapse of some structural components; the effort redistribution is not available in such cases and collapse is observed.The tree of failure, which is used to illustrate the system approach with reliability theory, may be composed by failure mechanisms associated in parallel or series manner.The system adopted in the beam analysed in this study is mixed, as it is composed by a parallel sequence (initial failure by bending) connected to a series sequence (initial failure due to shear effort), [27].Assuming that each failure path is a mutually exclusive event, the probability of global failure P f,syst is obtained by the sum of the probabilities of failure on each path, as follows: (16) To formulate the reliability problem, the following limit state functions were considered: (17) In which: M r and M a are, respectively, the resistant bending moment and the bending moment due to the loading.concerns the limit state function, in terms of bending moments, for point A, whereas indicates the limit state function, in terms of bending moments, for point B. V r and V a are the resistant shear effort and the shear force due to the loading, respectively.indicates the limit state function, in terms of shear, for point.The resistant efforts are obtained considering Equations 3 and 4. The efforts due to the applied load are obtained using Equations 15.

Effort redistribution. Hypothesis assumed
It is important to mention that the initial static scheme presented in Figure 3   Analogously to performed for point A, the difference between the bending moment due to the external load the resistant bending moment is reapplied into the structure.Then, considering this new static scheme, the bending moment at point A and the shear efforts along the beam span are recalculated in order to assess the violation of the conditional failure modes.The corrosion modelling was performed considering the propagation phase, i.e. the reinforcements area and yield stress are penalised after the corrosion time initiation.For each time step increment, the rebar area and yield stress are determined using Equation 7 and 9, respectively.After applying the corrosion effects, the limit state functions are recalculated in order to determine the failure path at each time increment (first individual failure mode and the conditional mode).As a result of such procedure, the individual probabilities of failure and the probability of global failure are assessed.Is important to emphasize that the internal stresses derived from the expansive corrosion reactions and the adherence loss between steel were not considered in the present study.

Results and discussion
The random parameters adopted in the probabilistic analyses are presented in Table 1.In addition to such parameters, it was also considered the following information, which were assumed as deterministic: n Water-cement ratio: 0.50; n Chloride concentration for reinforcements depassivation, C(y,t): 0.90 kg/m 3 [22]; n Chloride concentration at the beam surface, C 0 : 2.95 kg/m 3 [22]; n Concrete diffusion coefficient: [22]; n Total time considered in the analysis: 20 years; n Time increment to evaluate the strength capacity due to corrosion: 0.1 years; n Total number of Monte Carlo simulations: 3x10 6 .Figure 7 illustrates the evolution of reinforcement area along time.Due to corrosion phenomena, reinforcement area is lost along time.As illustrated in this figure, the reinforcement depassivation occurs after 11 years of the beam construction.From that time, denominated time for corrosion initiation, the corrosion propagation period starts.Then, the reinforcement area is penalized according to Equation 7. It is important to stress that reinforcement diameter reduction along time has linear behaviour, as presented in Equation 7. Consequently, the area reduction along time has quadratic behaviour.Figure 8 presents the evolution of the probability of failure considering each individual failure mode along time.In this figure, the probabilistic analyses were carried out accounting and disregarding the yield stress penalization on reinforcements along time.It is important to emphasize that, regarding Figure 8, the probability of failure of each initial failure mode changes along time.Therefore, the most probable failure path is not the same during all the time, as the most probable initial individual failure mode changes along time.
In the beginning of the propagation time, the most probable initial failure mode is [A].Such type of failure is, initially, obvious as the cross-section positioned at point A required the higher amount of reinforcement's area.However, as the corrosion process proceeds along time, the most probable failure scenario change.As presented in Figure 8, after 14 years of the beam construction, the failure mode [C] becomes the most probable initial failure mode.Such probabilistic behaviour is explained due to the stirrups diameter be lower than the longitudinal reinforcements diameter.Therefore, as presented in Equation 7, the stirrups lose cross-section area faster than longitudinal reinforcements along time.As a result of such cross-section lost, the failure on stirrups become more probable.This type of probabilistic behaviour illustrates the relevance/ importance of the present study.It shows that the mechanical behaviour intended during design phase may not be observed during the structural life.The mechanical structural behaviour can change drastically when corrosion effects are accounted.As presented in  The penalization of the reinforcement yield stress as a function of time did not introduce significant change into the probabilistic mechanical behaviour of the beam along time.The subtle difference concerns the time in which the mechanical effects due to the corrosion are observed.Considering the penalization of reinforcement yield stress, the mechanical effects of corrosion are observed earlier in comparison with analyses where such penalization was disregarded.
The behaviour of the probability of failure evolution along time regarding only the most probable failure path can also be analysed, leading to interesting results.Figure 9 presents the evolution of the probability of failure along time considering only the most probable failure path and disregarding the penalization of the reinforcements yield stress. Figure 10 presents similar results but accounting the penalization of the reinforcements yield stress.
The main difference among the results presented in Figure 9 and 10 relates the time in which the mechanical corrosion effects are observed.When the penalization of the reinforcements yield stress is accounted, the mechanical corrosion effects are earlier observed, as expected.However, any change is observed into the most probable failure paths, which are the same.Figure 11 illustrates the evolution of the probability of global failure along time.According to this figure, it can be observed important increase on the probability of global failure from, approximately, 16 years.Such global probabilistic behaviour indicates, as presented in Figures 9 and 10, that in this age, the mechanical effects due to the corrosion change the most probable failure path.The reduction on the reinforcements cross-section provided by corrosion phenomenon reduces the structural resistance.Consequently, the probability of global failure grows.It is important to observe that the probability of global failure always increase during the propagation period, which is consistent.

Conclusions
The main conclusions of the present study are the following: n The penalization on the reinforcement yield stress along time introduces mechanical degradation earlier than the case in which such penalization is disregarded.However, any change was observed regarding the structural global failure path.Then, the importance of considering such penalization concerns the extension of propagation period, which is lower when penalization is considered.In spite of its simplicity as the penalization model is based on empirical observations, the coupling of this approach in a nonlinear mechanical framework may lead to important changes into the mechanical structural behaviour.n The main conclusion of the present study concerns the change on the structural failure mode along time.The corrosion process provides reduction on the reinforcement's cross-section area along time.Then, the structural resistance changes along time as well as the initial failure mode and the structural collapse path.The knowledge about the most probable failure mode has major importance into a structural design, especially if maintenance, safety and failure prevention are focused.Considering a reinforced concrete structural design, bending moments and shear efforts lead to the determination of longitudinal reinforcements and stirrups areas, respectively.Then, the structural cross-sections more requested by the ex-ternal load receive higher reinforcement area.The structural engineer, intuitively, expects that the first failure mode occurs at the cross-section with higher reinforcement ratio, as such cross-sections are more requested.However, during the corrosion process, reinforcements area are lost, as previously mentioned.In addition to that, the corrosion process has more severe consequences in cross-sections with lower reinforcement ratios, as presented in the results of the present study.Then, during the corrosion phase, failure modes expected during design phase normally does not occur and failure modes in cross-section with lower reinforcement ratio appear.Therefore, the change on the failure modes during the propagation period is an important phenomenon that must be accounted in durability analyses in reinforced concrete structures in order to avoid unexpected failure modes.Finally, the present study supports further investigations that incorporates nonlinear mechanical models for concrete and steel, in order to consider realistic approaches to the efforts redistribution.Furthermore, the coupling of the probabilistic model to an optimization approach may also be interesting to determinate the optimal design solution that includes initial costs, maintenance and repair costs due to the change on the failure modes along time.

Acknowledgment
Sponsorship of this research project by São Paulo Research Foundation (FAPESP), grant number 2014/18928-2 is greatly appreciated.This research is a part of the activities scheduled by the research project USP/COFECUB 2012.1.672.1.0.

3 10
n+ .It means, in engineering structures, where the probability of failure is in between 3 10 − to 6

Figure 2 -Figure 3 -Figure 4 -
Figure 2 -Monte Carlo simulation method.General scheme considering two random variables and two limit state functions is valid for the determination of the first individual failure mode, i.e. events [A], [B] and [C] on the tree of failure.After the first individual failure mode be violated, effort redistribution may be assumed.As previously mentioned, shear failure is brittle and normally leads to the structural collapse.Therefore, when the first individual failure mode violated is the mode [C], structural failure is assumed.However, the first individual failure being modes [A] and [B], which characterize bending failures, effort redistribution has to be performed.If individual failure mode [A] is firstly observed, a perfect plastic hinge is assumed to appear at point A. The mechanical effect of such new condition is introduced by reapplying the difference between the bending moment due to the external load and the resistant bending moment at point A, which characterizes a new static scheme.Then, in this new static scheme, the positive bending moments and shear efforts considering the exceeding bending moment at point A are recalculated along the beam and the failure of the conditional failure modes is assessed.When the first individual failure mode observed is [B], first level on the tree of failure, a perfect plastic hinge is introduced at point B.

Figure 5 -Figure 6 -
Figure 5 -Failure modes defined by the respectively cross-sections

Figure 7 -
Figure 7 -Evolution on the rebar cross-section during the corrosion process Figure 8 -Evolution on the probability of failure considering individual failure modes

Figure 8 ,
Figure 8, sudden brittle failures due to shear effort may appear before the expected ductile bending failures.After 16.5 years from the beam construction, the individual failure mode [B] becomes the most probable initial failure mode, as presented in Figure 8.Such change is explained due to the longitudinal reinforcements cross-section lost along time caused by corrosion.Thus, the faster decrease of the longitudinal reinforcement's cross-section along time at point B in comparison with point A and stirrups increases significantly the importance of such initial failure mode.As the reinforcement area along the beam change due to the corrosion, the structural configuration change, the resistant mechanisms change and, consequently, the failure modes also change.Another important behaviour that must be commented concerns the reduction of the probabilities of failure in individual modes [A] and [C].The probabilities of failure presented in Figure 8 relate only the probability of failure of each individual failure mode.Therefore, conditional probabilities of failure were not considered in the construction of such figure.Then, it explains the reduction on individual failure modes [A], after 14.5 years, and [C], after 18.5 years.It is important to emphasize that at each time increment at least one individual failure mode had its individual probability of failure increased (during the propagation period obviously).It is consistent regarding probabilistic analyses and make consistent the analyses performed.

Figure 11 -
Figure 11 -Evolution on the probability of failure considering global failure

Table 1 -
Statistic properties for random variables