Diameter dependence of tensile strength by Weibull analysis: Part I bamboo fiber

Abstract

Fibers stripped of from the bamboo culm by longitudinal cutting are being considered as reinforcement of polymer composites owing to environmental benefits related to their biodegradable and renewable characteristics. The manual cutting process allows bamboo fibers with different diameters to be extracted from the culm. Since a lignocellulosic fiber usually presents tensile strength dependence with its diameter, this possibility was investigated on bamboo fibers by means of the Weibull statistical analysis. It was found that the smaller the fiber diameter, the greater the tensile strength. Fracture observation of ruptured bamboo fibers by scanning electron microscopy, identified possible mechanisms associated with this inverse strength/diameter correlation.

Bamboo fibers; tensile strength; diameter dependence; Weibull analysis


Diameter dependence of tensile strength by Weibull analysis: Part I bamboo fiber

L.L. da Costa; R.L. Loiola; S.N. Monteiro

Advanced Materials Laboratory, LAMAV, State University of the Northern Rio de Janeiro, UENF, CEP28013-602, Campos dos Goytacazes, RJ. e-mail: luclopes_@hotmail.com; romuloakira@gmail.com; sergio.neves@ig.com.br

ABSTRACT

Fibers stripped of from the bamboo culm by longitudinal cutting are being considered as reinforcement of polymer composites owing to environmental benefits related to their biodegradable and renewable characteristics. The manual cutting process allows bamboo fibers with different diameters to be extracted from the culm. Since a lignocellulosic fiber usually presents tensile strength dependence with its diameter, this possibility was investigated on bamboo fibers by means of the Weibull statistical analysis. It was found that the smaller the fiber diameter, the greater the tensile strength. Fracture observation of ruptured bamboo fibers by scanning electron microscopy, identified possible mechanisms associated with this inverse strength/diameter correlation.

Keywords: Bamboo fibers, tensile strength, diameter dependence, Weibull analysis.

1 INTRODUCTION

Bamboo is a well known grass-type plant with a hard and stiff stem or culm that can reach, in some species, more than 10 cm in cross section diameter and stand several meters height. Owing to its low density, approximately 0.9 g/cm3, bamboo culms have been used in house construction from scaffoldings to panels. As an abundant natural resource in tropical and temperate regions, specially in Asia and South America, bamboo is also a substitute for wood and plastics in furniture and lightweight parts of automobile [1, 2]. The cylindrical shape of the culm is, however, a limitation for its direct use in engineering systems. Consequently, research works have been conducted on bamboo fibers stripped off from the culm as reinforcement of polymer composites. [1-12]. According to SHIN et al. [3] bamboo fiber-epoxy laminates can be made into specific sizes and shapes, preserving the natural microstructural properties. These fiber composites overcome the limitation of the culm's cylindrical macrostructure. As a further advantage, SHIN et al. [3] indicated that cracking and bioerosion caused by insect pests is prevented.

Works on the mechanical properties of polymer composites reinforced with culm-stripped bamboo fibers [3-5, 12] reported mechanical strength and modulus that could vary significantly with the amount of incorporated fiber, the type of polymeric matrix and the fiber disposition (short-cut, continuous, aligned, mat-arranged). In spite of all these efforts, no investigation on the influence of the fiber diameter has yet been carried out. Owing to the oriented lignocellulosic structure, as in other natural fibers [13-16], it is relevant to investigate how the mechanical behavior of the bamboo fibers is affected by its cross section diameter.

Depending on the specialist ability and cutting technique, the manual culm stripping off process produces bamboo fibers with different diameters. Therefore, the objective of this work was to investigate the bamboo fiber tensile strength dependence on its diameter using a Weibull statistic analysis.

2 EXPERIMENTAL PROCEDURE

The basic material used in this work was the culm of bamboo (Bambusa vulgaris) supplied by a producer of the north region of Rio de Janeiro, southeast of Brazil. Large bamboo bushes, Figure 1(a), occur naturally in the region and are locally used as fence and home utensils. Fibers were manually stripped off from dried culms, Figure 1(b) with a sharp razor blade. The longitudinal direction of the fiber coincides with that of the culm and corresponds to the natural direction of the bamboo cellulose fibrils. Different cross section diameters were obtained, Figure 1(c), in spite of the apparently uniform manual stripping procedure. From randomly selected 100 fibers, the equivalent diameter corresponding to the average between the larger and smaller (90º rotation) cross section dimensions at five locations for each fiber, was measured in a profile projector.


The histogram in Figure 2 shows the frequency of diameter distribution of stripped bamboo fibers used in the present work. Based on this histogram, an average diameter of 0.56 mm was calculated within the interval from 0.3 to 0.9 mm.


The as-stripped bamboo fibers, Figure 1(b), were dried in a laboratory stove at 60 C for 24 hours to remove humidity. For each interval of equivalent diameter in Figure 2, 20 fibers were selected. All these fibers were then individually tensile tested at 25 ± 2ºC in a model 5582 Instron machine. Specials grips were used to avoid both fiber slippage and damage. The test length was 8 cm and the strain rate 2.1x10-4s-1. Values obtained for the tensile strength, i.e. the ultimate stress, were statistically interpreted by means of a Weibull Analysis computer program.

The tensile-ruptured tip of some tested fibers were attached with conducting carbon tape to a metallic support and then gold sputtered for scanning electron microscopy (SEM) observation in a model SSX-550 Shimadzu equipment operating with secondary electrons accelerated at a maximum voltage of 15kV.

3 RESULTS AND DISCUSSION

Figure 3 exemplifies typical load vs. elongation curves obtained, for each diameter interval in Figure 2, through digital recorded data acquired by the Instron system. In these curves it should be noticed some common aspects and subtle differences. In common, the curves present an initial linear elastic behavior followed by an abrupt rupture with no apparent plastic extension. Consequently, for all diameter intervals, the culm-stripped bamboo fiber can be considered as a brittle material. In terms of differences, the tensile curves for fibers thinner than 0.5mm display small oscillations in the load, which can be attributed to minor instabilities in the deformation of heterogeneous lignocellulosic fibers. On the other hand, fibers thicker than 0.6mm show serrations associated with few larger drops along the curve. In principle, these serrations and drops could be associated with partial rupture of the bundle of fibrils that compose the bamboo structure [2]. As further discussed, it is important to mention that the thinner the bamboo fiber, the lesser fibrils it contains.


Based on the maximum load attained in the curve, like the ones exemplified in Figure 3, the tensile strength, corresponding to the ultimate stress (σm) was determined for each fiber. The values of σm were then statistically analyzed by means of the Weibull method for the 20 fibers associated with everyone of the six diameter intervals shown in the histogram of Figure 2. The Weibull Analysis program provided the probability plots of reliability vs. location parameter shown in Figure 4 for all diameter intervals. Here it should be noted that all plots in Figure 4 are unimodal, i.e. with just one single straight line fitting the points at each interval. This indicates similar mechanical behavior of fibers within the same diameter interval.


In addition, the program also provided the corresponding characteristic stress (θ), the Weibull modulus (β) and the precision adjustment (R2) parameters. The values of these parameters as well as the average mechanical strength and associated statistical deviations, based on the Weibull distribution, are presented in Table 1.

The variation of the characteristic stress with the average fiber diameter for each one of its intervals is presented in Figure 5. In this figure there is a tendency for the θ¸ parameter to vary inversely with the average bamboo fiber diameter. This means that the thinner the fiber the higher tends to be the characteristic stress. Furthermore, the corresponding values of β and R2, shown in Table 1, statistically support the inverse correlation between θ and the average diameter d (mm). By means of a mathematic correlation, a hyperbolic type of equation was proposed to fit the data in Figure 5.


In order to analyze the physical meaning of Equation (1), the average tensile strength, , evaluated in this work for the culm-stripped bamboo fibers was plotted as a function of the diameter in Figure 6. In this figure an apparent hyperbolic inverse correlation also exists between and d within the error bars (statistical deviations) and investigated limits.


Here it is important to mention that the large dispersion (error bars) in the values of the tensile strength in Figure 6 is due to the heterogeneous characteristics of any lignocellulosic fiber [18], such as the bamboo in this work. As a consequence, one could also consider a horizontal line passing within the error bars as a possible correlation between and d. In this case, the tensile strength would not vary with the diameter. However, the variation of θ with d in Figure 5, suggests that an inverse correlation fits better the experimental results for the bamboo fibers.

It is also possible to consider that the values of in Figure 6 are approximately constant, around 100 MPa, for fiber thicker than 0.5mm. Under this consideration, only the thinner bamboo fibers, d < 0.5mm, present the inverse correlation, but not necessarily hyperbolic. This should be further investigated.

Based on Equations (1) and (2) it is suggested that, as in others lignocellulosic fibers [16, 17], a hyperbolic type of mathematical equation is the best statistical correlation between the tensile strength and the diameter of culm-stripped bamboo fibers.

A SEM observation of the tip of representative tensile-ruptured fibers, shown in Figure 7, provided further evidence of a fracture mechanism that could justify the hyperbolic correlation in Equation (2). With the same magnification, the thinner fiber, Figure 7(a), shows a more uniform fracture associated with lesser fibrils. By contrast, a fiber with larger diameters, Figure 7(b), displays a relatively non-uniform fracture with participation of more fibrils. Statistically, there is always a chance that one of the many fibrils of the thicker bamboo fiber in Figure 7(b), would prematurely break and then act as a flaw to cause the fiber rupture at a lower stress as compared to the thinner fiber, Figure 7(a). In other words, the larger distribution of fibrils strength of the thicker fiber allows one of them breaking shortly than any of the fewer fibrils of a thinner fiber.


As a final remark, it should be mentioned that an inverse correlation such as that in Equation (2), could allow, in practice, a selection of stronger culm-stripped thinner bamboo fibers to effectively reinforced polymer composites with improved mechanical properties.

4 CONCLUSIONS

A Weibull statistical analysis of tensile-tested manually culm-stripped bamboo fibers revealed an inverse correlation between the stress and the fiber diameter.

This correlation indicates a possible hyperbolic mathematical equation to hold, at least, for diameters below 0.6mm.

SEM observations provided evidences that a thicker bamboo fiber, with more fibrils than a thinner one, could undergo rupture at a comparatively lower stress.

Statistically, the larger distribution of fibrils mechanical resistances of the thicker fiber allows a weaker fibril to rupture shortly than any of the fewer fibrils of the thinner fiber.

5 ACKNOWLEDGEMENTS

The authors thank the support to this investigation by the Brazilian agencies: CNPq, CAPES, FAPERJ and TECNORTE/FENORTE.

6 REFERENCES

Data de envio: 20/03/2010

Data de aceite: 20/06/2010

Autor Responsável: Sergio Neves Monteiro

  • [1] CHEN, X., GUO, Q., MI, Y., "Bamboo fiber reinforced polypropylene composites: a study of the mechanical properties", Journal Applied Polymer Science, v. 69, pp. 1891-1899, 1998.
  • [2] SHIBATA, S., YONG, C., FUKUMOTO, I., "Flexural modulus of the unidirectional and random composites made from biodegradable resin and bamboo and kenaf fibres", Composites Part A, v. 39, pp. 640-646, 2008.
  • [3] SHIN, F.G., XIAN, X.J., ZHENA, W.P., YIPP, M.W., "Analysis of the mechanical properties and microstructure of bamboo epoxy composites", Journal Materials Science, v. 24, pp. 3483-3490, 1989.
  • [4] JAIN, S., KUMAR, R., JINDAL, U.C., "Mechanical behavior of bamboo and bamboo composites", Journal Materials Science, v. 27, pp. 4598-4604, 1992.
  • [5] JAIN, S., KUMAR, R., JINDAL, U.C., "Development and fracture mechanism of the bamboo/polyester resin composite", Journal Materials Science Letters, v. 12, pp. 558-560, 1993.
  • [6] SEEMA, J., KUMAR, R., "Processing of bamboo fiber reinforced plastics composites", Materials Manufacture & Processing, v. 9, pp. 813-828, 1994.
  • [7] THWE, M.M., LIAO, K., "Effects of environmental aging on the mechanical properties of bamboo glass fiber reinforced polymer matrix hybrid composites", Composites Part A, v. 33, pp. 43-52, 2002.
  • [8] OKUBO, K., FUJII, T., YAMAMOTO, Y., "Development of bamboo based polymer composites and their mechanical properties", Composites Part A, v. 35, pp. 377-383, 2004.
  • [9] OKUBO, K., FUJII, T., YAMASHITA, N., "Improvement of interfacial adhesion in bamboo polymer composite enhanced with micro-fibrillated cellulose", JSME International Journal A. Solid M., v. 48, pp. 199-204, 2005.
  • [10] LEE, S.H., WANG SIQUN, "Biodegradable polymer/bamboo fiber biocomposite with bio-based coupling agent", Composites Part A, v. 37, pp. 80-91, 2006.
  • [11] HUANG, X., NETRAVALI, A., "Biodegradable green composites made using bamboo micro/nano-fibrils and chemically modified soy protein resin", Composites Science & Technology, v. 69, pp. 1009-1015, 2009.
  • [12] COSTA, L.L., MONTEIRO, S.N., LOIOLA, R.L., "Mechanical behavior of polyester composites reinforced with continuous bamboo fibers", In: Proceedings of the Characterization of Minerals, Metals & Materials - TMS Conference 2010, pp. 1-6, Seattle, WA, USA, February 2010.
  • [13] KULKARNI, A.G., SATYANARAYANA, K.G., ROHATGI, P.K., VIJAYAN, K., "Mechanical properties of banana fibers", Journal of Materials Science, v. 18, pp. 2290-2296, 1983.
  • [14] MURHERJEE, P.S., SATYANARAYANA, K.G., "Structure and properties of some vegetable fibers", Journal of Materials Science, v. 21, pp. 51-56, 1986.
  • [15] TOMCZAK, F., SATYANARAYANA, K.G., SYDENSTRICKER, T.H.D., "Studies on lignocellulosic fibers of Brazil Part III - Morphology and properties of Brazilian curauá fibers", Composites: Part A, v. 38, pp. 2227, 2007.
  • [16] MONTEIRO, S.N., SATYANARAYANA, K.G., LOPES, F.P.D. "High strength natural fibers for improved polymer matrix composites", Materials Science Forum, v. 638-642, pp. 961-966, 2010.
  • [17] NASCIMENTO, D.C.O., MOTTA, L.C., MONTEIRO, S.N., "Weibull analysis of tensile tested piassava fibers with different diameters", In: Proceedings of the Characterization of Minerals, Metals & Materials - TMS Conference 2010, pp. 1-8, Seattle, WA, USA, February 2010.
  • [18] MONTEIRO, S.N., LOPES, F.P.D., FERREIRA, A.S., NASCIMENTO, D.C.O., "Natural fiber polymer matrix composites: cheaper, tougher and environmentally friendly", JOM - The Member Journal of TMS, v. 61, n. 1, pp. 17-22, 2009.

Publication Dates

  • Publication in this collection
    27 Aug 2010
  • Date of issue
    2010

History

  • Accepted
    20 June 2010
  • Received
    20 Mar 2010
Laboratório de Hidrogênio, Coppe - Universidade Federal do Rio de Janeiro, em cooperação com a Associação Brasileira do Hidrogênio, ABH2 Av. Moniz Aragão, 207, 21941-594, Rio de Janeiro, RJ, Brasil, Tel: +55 (21) 3938-8791 - Rio de Janeiro - RJ - Brazil
E-mail: revmateria@gmail.com