This work had as objective to establish de best brazing parameter to joint Al2O3 pre-metalized with Ti by plasma process using amorphous ribbons of Cu49g45Ce x alloys as filler metals. The alloys were prepared in arc furnace and processed by melt-spinning process varying the Ce percentiles from 4 to 6. % . The brazing was accomplished in vacuum furnace and the following variables analyzed: deposition time of Ti film, brazing temperature and brazing times which were related to the brazed joint 3-point bending resistance. The interaction between those factors was obtained by linear regression equation. The metalized ceramic surfaces presented an good uniformity and the joint a very good adhesion reaching bending resistance up to 176,8 MPa.
Al2O3 brazing; Amorphous ribbons; Bending resistance; plasma metallization