Physicochemical Properties of Root Canal Filling Materials for Primary Teeth

Abstract

This study evaluated physiochemical proprieties of a calcium hydroxide-based paste (Calen(r)) combined with a zinc oxide cement at different ratios (1:0.5, 1:0.65, 1:0.8 and 1:1). Materials were compared regarding setting time, pH variation, radiopacity, solubility, dimensional changes, flow and release of chemical elements. Data were analyzed statistically by ANOVA and Tukey's test (α=0.05). Longer setting time and higher dimensional changes and solubility values were exhibited by 1:0.65 and 1:0.5 ratios (p<0.05). The 1:0.5 and 1:0.65 ratios exhibited the highest pH values at all time points. All materials exhibited high radiopacity values. Significant differences were found only between 1:0.5 and 1:1 ratios for calcium and zinc release (p<0.05), whereas the amount of zirconium was similar among all groups (p>0.05). Considering the evaluated proprieties, combinations of Calen(r) paste with ZO at 1:0.5 and 1:0.65 ratios had the best results as root canal filling materials for use in primary teeth.

Key Words:
filling materials; primary teeth; calcium hydroxide; pH; radiopacity; setting time; dimensional changes; solubility.

Fundação Odontológica de Ribeirão Preto Av. do Café, S/N, 14040-904 Ribeirão Preto SP Brasil, Tel.: (55 16) 3602-3982, Fax: (55 16) 3633-0999 - Ribeirão Preto - SP - Brazil
E-mail: bdj@forp.usp.br