ABSTRACT
Objective
Evaluate the influence of silane heat treatment in bond durability between two resin cements and CAD/CAM feldspathic ceramic.
Methods
40 feldspathic ceramic blocks were obtained, and were duplicated in microhybrid composite. All ceramic blocks were etched with 10% hydrofluoric acid for 20 s and received application of silane agent. The blocks were randomizedinto eight groups (n=5) according to the surface treatments and luting agents: P- Panavia F; PAg- Panavia F + Aging; HP- Heat Treatment + Panavia F; HPAg- Heat Treatment + Panavia F + Aging; R- RelyX ARC; Rag- RelyX ARC + Aging; HR- Heat Treatment + RelyX ARC; HRAg- Heat Treatment + RelyX ARC + Aging. The heat treatment was performed in furnace at 100 °C for 2 min. All blocks were cemented and cut to obtain samples with adhesive area of 1 mm2. Aging was performed with 10000 thermal cycles. The samples were subjected to microtensile bond strength test.
Results
The three-way ANOVA test revealed a significant interaction between cement versus heat treatment (p=0.001) and heat treatment versus thermal cycling (p=0.001) indicating that there was a change in bond strength due to surface treatment and aging.
Conclusion
Therefore, the heat treatment of the silane at 100 ºC for 2 minutes obtained higher values of bond strength between the resin cement and a feldspathic ceramicafter aging.
Indexing terms
Aging; Ceramic; Tensile strength; Thermic treatment