Abstract
When AISI 316L stainless steels are submitted to the nitriding process at temperatures lower than 450 °C, a high nitrogen content expanded austenite phase is formed, which shows higher hardness and higher pitting corrosion resistance compared to the untreated material. As a result, this material becomes adequate for biomedical application. The conditions of the nitriding technique, such as gas mixture, pressure, time and temperature, play an important role in some properties of the modified layer, including: thickness, hardness and N concentration along the layer. This paper explores a set of six samples of AISI 316L, nitrided at different times and temperatures, whose properties show important differences. The aim of this research is to investigate the correlation between the nitrided layer thickness (in the range of 0.77 to 11 µm) with both X-ray patterns characteristics and hardness measurements, which used two distinct loads. The results of this study show that: whereas the 3.6 gf load was suitable to measure the real hardness for four of the nitrided layers showing thickness ≥ 2.9 µm, the 50 gf load measured a substrate contribution, probably even for the highest thickness, 11 µm. Moreover, analyzing different reflections of the X-ray patterns showed evidence of the clear consistency between the X-Ray depths and the nitrided layer thicknesses: if the layer thickness is lower than the penetration depth of X-rays, two phases (austenite and expanded substrate) are present. If the layer thickness is higher, only the austenite is observed. Finally, concerning the citotoxicity property, all the samples, nitrided or not, were approved in the test for biocompatibility, indicating their potential use for biomedical applications.
AISI 316 L; plasma nitriding; layer thickness; hardness; X- ray diffraction; citotoxicity
Investigating the correlation between some of the properties of plasma nitrided AISI 316L stainless steel
M. Olzon-DionysioI,* ; M. CamposI; O. Z. HigaII; T. F.da CunhaII; S. D. de SouzaI
IPhysics Department, Federal University of São Carlos - UFSCar, CEP 13565-905, São Carlos, SP, Brazil
IIBiotechnology Center, Energy and Nuclear Research Institute - IPEN, CEP 05508-000, São Paulo, SP, Brazil
ABSTRACT
When AISI 316L stainless steels are submitted to the nitriding process at temperatures lower than 450 °C, a high nitrogen content expanded austenite phase is formed, which shows higher hardness and higher pitting corrosion resistance compared to the untreated material. As a result, this material becomes adequate for biomedical application. The conditions of the nitriding technique, such as gas mixture, pressure, time and temperature, play an important role in some properties of the modified layer, including: thickness, hardness and N concentration along the layer. This paper explores a set of six samples of AISI 316L, nitrided at different times and temperatures, whose properties show important differences. The aim of this research is to investigate the correlation between the nitrided layer thickness (in the range of 0.77 to 11 µm) with both X-ray patterns characteristics and hardness measurements, which used two distinct loads. The results of this study show that: whereas the 3.6 gf load was suitable to measure the real hardness for four of the nitrided layers showing thickness ≥ 2.9 µm, the 50 gf load measured a substrate contribution, probably even for the highest thickness, 11 µm. Moreover, analyzing different reflections of the X-ray patterns showed evidence of the clear consistency between the X-Ray depths and the nitrided layer thicknesses: if the layer thickness is lower than the penetration depth of X-rays, two phases (austenite and expanded substrate) are present. If the layer thickness is higher, only the austenite is observed. Finally, concerning the citotoxicity property, all the samples, nitrided or not, were approved in the test for biocompatibility, indicating their potential use for biomedical applications.
Keywords: AISI 316 L, plasma nitriding, layer thickness, hardness, X- ray diffraction, citotoxicity
1. Introduction
The practice of using metals and alloys to repair or replace human body parts is now well established. Two of the most important parameters in determining the suitability of a material for biomedical applications are its biocompatibility and corrosion resistance1-3. Regarding these two parameters, pure titanium appears to be almost the perfect biomaterial, but it is still essential to provide high strength or ductility for many surgical and dental applications. Hence, materials such as stainless steels2-4, particularly ASTM F138 and AISI 316L, have been used as alternative materials. The corrosion resistance and hardness of these alloys are inadequate for this application, but if they are submitted to an adequate nitriding process, these properties can be improved5-8. When nitriding is performed at temperatures lower than 450 °C a high nitrogen content expanded austenite phase is formed, which shows higher hardness and higher pitting corrosion resistance compared to the untreated material7-10. The conditions of the nitriding technique (gas mixture, pressure, time and temperature) play an important role in the characteristic of the modified layer7,11,12, as thickness, hardness and N concentration along the layer. Although extensive research has been carried out on plasma nitriding of stainless steels, researchers have not explored in much detail the correlation between both, the nitrided layer thickness and hardness measurements or X-ray patterns characteristics. The aim of this work is to cover this aspect adequately. In order to produce nitrided layers with different characteristics, six samples of AISI 316L austenitic stainless steel were nitrided at different times (3 and 5 h) and temperatures (350 °C, 400 °C and 450 °C). Results of nitrided layers thickness, hardness, X-ray diffraction patterns and the correlation between them are presented here. Some results of citotoxicity are also reported.
2. Material and Methods
Samples: In this study, AISI 316L stainless steel produced by Villares Metals was used. Its chemical composition (only elements with wt.% > 0.10) is: 16.1 ± 0.2 Cr, 10.1 ± 0.1 Ni, 2.1 ± 0.1 Mo, 1.80 ± 0.02 Mn, 0.37 ± 0. 05 Si, 0.31 ± 0.04 Cu, 0.180 ± 0.004 W, 0.13 ± 0.01 Co, balance Fe. The samples (diameter: 19.70 ± 0.05 mm, thickness: 3.85 ± 0.05 mm) were sanded using sandpaper from 220 to 1 200 mesh, polished with alumina (0.3 and 1 µm), cleaned ultrasonically in an acetone bath, and finally air-dried. Next, they were plasma nitrided in cold wall equipment using d.c. power supply. The gas composition was 80% H2-20%N2, at a pressure of about 6 torr. The voltage and current density were adjusted to maintain the cathode temperature (or nitriding temperature). The temperature was measured using an alumel-chromel (type K) long rod thermocouple placed underneath the sample. Three different temperatures (350 °C, 400 °C and 450 °C) were used at two different nitriding times, 3 and 5h.
Scanning Electron Microscopy: A section of the samples were observed using a JEOL scanning electron microscope, JSM - 5800 LV model in order to measure the depth of the nitrided layer.
Hardness: The surface hardness was measured using a Leica microhardness tester (model VMHT-MOT) with a Vickers indenter at a load of 50 gf. The hardness was measured at about 20 different positions along the diameter, aiming at achieving more representative results. Each position was repeated three times at a distance of 20 ± 2 µm from one to the other. Other measurements of hardness, which were done along the diameter, equally spaced of 0.25 mm, were done using a Fischerscope H100V microhardness tester with a Vickers indenter at a load of 35 mN (~3.6 gf). Due to the low load used in the last one, a special computational routine, which was developed for treating similar data, was used on the data treatment13.
X- ray diffraction: X-ray diffraction patterns of untreated and nitrided samples were obtained using a Rigaku (Geigerflex model) diffractometer, Cu Kα radiation (λ = 0.154056 nm). The conditions were: 2θ scan step 0.02°, ranging from 30° to 100°, 2 s counting time.
Cytotoxicity test: Following the guidelines of ISO 10993-5[14], the cytotoxicity test was performed in culture microplates seeded with CHO cells and sample extracts diluted from 100 to 6.25%[15]. The microplates were incubated for 72 h at 37 °C in a humidified 5% CO2 atmosphere. The cell viability was measured by adding 20 µL of MTS/PMS (20:1) solution and incubated for 2 h in the CO2 incubator. The microplates were read in a spectrophotometer reader at 495 nm. The results were compared with a negative control of titanium and a positive control of phenol 0.3% in saline solution. The Inhibitory Concentration for 50% of cell viability was taken from graphs.
3. Results and Discussions
3.1. Nitrided layer thickness and hardness measurements
Figure 1a, b show the Scanning Electronic Microscopy (SEM) micrographs of the sample nitrided at 450 °C for 5 h to illustrate the measurements of nitrided layer thickness t. The arithmetic mean value of 6 measurements, which were done for all the nitrided samples, are shown in the 3rd column of Table 1. Based on this values, one can see that thickness increases up to a factor of 9.5 and 11 in the temperature interval (350 °C to 450 °C) for both t=3h and t=5h, respectively. It seems to indicate that the thickness of the nitrided layer is primarily a function of temperature12,16. Similar behavior was observed in a previous study on AISI 304, where the thickness increased from 2-3 to 30 µm for practically the same temperature interval (350 °C to 460 °C)16.
Some characteristics and properties of the nitrided layers: nitrided layer thickness (t), mean value of hardness and mean value of penetration depth (p) of the Vickers indenter.
SEM micrographs of sample nitrided at 450 °C, for 5 h (a) near the edge, (b) in the central region.
Concerning hardness measurements, Figure 2a, b illustrate the hardness measurements for both loads on the surface of the samples nitrided for 3 h. The mean values, which are represented by a dashed line in the Figures 2, are shown in the 4th and 6th columns of Table 1 for all the samples. For the untreated sample, this value is 243 ± 40 HV0.05 and 298 ± 19 HV0.0036, for loads of 50 and 3.6 gf, respectively.
Hardness measurements on surface samples nitrided for 3h, from the border to the center, at different temperatures, using different loads (a) 3.6 gf, (b) 50 gf.
The penetration depth p of the Vickers indenter was estimated from the length of the diagonal line across the indent marked on each sample. The mean values are presented in the 5th and 7th columns. Figure 3a, b depict hardness values as a function of the ratio between penetration depth p and nitrided layer thickness t, for both load, 3.6 gf and 50 gf, respectively. In these figures, the position of p/t = 1/7[17], which is the ratio indicated to avoid the influence of substrate, is marked as a dashed line. On the left of this line in Figure 3a, there is compatibility among the hardness values, which were measured for the four samples, which were prepared at 400 °C and 450 °C. So, the values showed on the left of the dashed line in Figure 3a seem to represent essentially real hardness of the nitrided layers, which reached an improvement of a factor by 6 times compared to the substrate. This result is compatible with some previous, when the authors found hardness value of 17 GPa (~1733 HV)18.
Hardness value as function of ratio between penetration depth p and nitrided layer thickness t, using different loads (a) 3.6 gf (b) and 50 gf.
However, in Figure 3a, for the 350 °C samples, which show thinner layer, there is some substrate contribution. Such contribution is much more significant for all the measurements in Figure 3b, where practically all the p/t values are on the right of the dashed line. Nevertheless, even at the highest load (50 gf), for the less favorable sample (3h), the hardness is about 160% of the one measured for the substrate.
3.2. X-ray Diffraction (XRD)
The X-ray diffraction pattern for the AISI 316L samples before and after nitriding for 3h are shown in Figure 4. All the samples nitrided show the expanded austenite peaks, which are broader and shifted to lower diffraction angles, when compared to the austenitic substrate.
X-ray diffraction patterns of samples untreated and nitrided for 3h at different temperatures.
The samples nitrided at 350 °C clearly show the substrate peaks, which apparently seems not to occur for 400 °C and 450 °C. However, this is not true and we can obtain relevant information about the N concentration, if we analyze, for example, a reflection where there are different ratios between the X-ray depth d and the layer thickness t (d/t). For this purpose, let us consider two different reflections.
First, let us take the (111) reflection, at 43.7° position, for example. A zoom of this peak is shown in Figure 5a, b, for the samples nitrided at 3 and 5h. If 99% absorption of X-ray in the sample is considered, in this configuration Ө-2Ө, the X-ray penetration depth d is approximately 4 µm19. As the ratio d/t < 0.52 for 450 °C and d/t ≥ 4 for 350 °C, the γ(111) intensity is negligible for the first sample and very significant for the last one. On the other hand, for 400 °C, the thickness values are compatible (whitin the measurement precision) for 3 and 5h and are also close to d. Because of this, the γ(111) intensity is quite small for both samples, 3 and 5h.
Zoom of the (111) reflection of samples nitrided at different temperatures for (a) 3h and (b) 5h.
Moreover, since as the more distant from the 43.7° (position of substrate (111) reflection), the greater the N concentration in the corresponding sample is, it can be said that Figure 5a, b show that if the temperature increases from 350 to 450 °C, the N concentration increases, for 3 and 5h.
Secondly, in order to obtain some indications from the N concentration at a higher depth, let us analyze the expanded austenite (220) reflection, whose d ~ 7 µm, considering a X-ray absorption of 99%, as before19. For this purpose, Figure 6 compares the presence of the substrate (220) line, for the samples nitrided for 3h. Even though the statistics is not so good at this peak, it is sufficient to indicate an interesting aspect: for 350 °C, whose d/t = 9.09, practically there is no broad peak at 2θ < 74.8, which is the position of the substrate (220) line, while for 400 °C, whose d/t = 2.41, there are both: the substrate line and the broad peak, centered at approximately 2θ =71°. On the other hand, only this broad peak is present for 450 ºC, where d/t = 0.92 and is centered at approximately 2θ = 69°. Therefore, the last sample presents a larger N concentration of the expanded austenite than the both samples treated at lower temperatures.
Therefore, it can be observed that these comparisons show evidence of the clear consistency between the X-Ray depths d and the nitrided layer thicknesses t.
3.3. Citotoxicity measurements
The cell viability determinations of all the samples are very similar. The curves obtained for untreated and nitrided at 350 °C are shown in Figure 7. All the samples did not present any toxicity effect similar to the negative control (IC50>100), showing their harmless character. The cytotoxicity test in the biological evaluation is a toxicological screening test that can predict the biocompatibility of 316 L stainless steel, if nitrided or not. This is a primary indication of their potential use for biomedical applications.
Cell viability of positive and negative control in detail; samples untreated and nitrided at 350, 400 and 450 ºC.
4. Conclusion
The purpose of the current paper was to correlate the nitrided layer thickness t of a set of six samples with: i) The penetration depth of the indenter Vickers for two different load (3.6 gf and 50 gf); ii) Two different penetration depths (approximately 4 and 7 µm) of the X-ray. The results of this investigation show that:
The 3.6 gf load was suitable to measure the real hardness of four of the nitrided layers, which show t ≥ 2.9 µm. On the other hand, the 50 gf load measures a substrate contribution, probably even for the highest t, 11 µm;
Analyzing different reflections of X-ray patterns showed that if the layer thickness is lower than the penetration depth of X-rays two phases (austenite and expanded substrate) are present. On the other hand, if the layer thickness is higher, only the austenite is present.
Moreover, concerning citotoxicity, all the samples, nitrided or not, were approved in the first test for biocompatibility, indicating their potential use for biomedical applications.
Acknowledgements
We would like to thank Dr. J. M. D. A. Rollo and Leandro J. de Paula for support in the hardness measurements and Dr. Solange de Souza for her interest in the citotoxicity measurements. Moreover, we are grateful to the technical collaborator Natália A. Zanardi. This work was partly supported by the Brazilian research funding agencies FAPESP and CAPES.
Received: September 27, 2012
Revised: February 19, 2013
References
- 1. Geetha M, Singh AK, Asokamani R and Gogia AK. Ti based biomaterials, the ultimate choice for orthopaedic implants- A review. Progress in Materials Science 2009; 54:397-425. http://dx.doi.org/10.1016/j.pmatsci.2008.06.004
- 2. Lei MK and Zhu XM. In vitro corrosion resistance of plasma source ion nitrided austenitic stainless steels. Biomaterials 2001; 22:641-647. http://dx.doi.org/10.1016/S0142-9612(00)00226-X
- 3. Antunes RA, Rodas ACD, Lima NB, Higa OZ and Costa I. Study of the corrosion resistance and in vitro biocompatibility of PVD TiCN-coated AISI 316L austenitic stainless steel for orthopedic applications. Surface and Coatings Technology 2010; 205:2074-2081. http://dx.doi.org/10.1016/j.surfcoat.2010.08.101
- 4. Bordji K, Jouzeau J-Y, Mainard D, Payan E, Delagoutte J-P and Netter P. Evaluation of the effect of three surface treatments on the biocompatibility of 316L stainless steel using human differentiated cells. Biomaterials 1996; 17:491-500. http://dx.doi.org/10.1016/0142-9612(96)82723-2
- 5. Li G-J, Peng Q, Li C, Wang Y, Gao J, Chen S-Y et al. Effect of DC plasma nitriding temperature on microstructure and dry-sliding wear properties of 316L stainlesssteel. Surface and Coatings Technology 2008; 202:2749-2754. http://dx.doi.org/10.1016/j.surfcoat.2007.10.002
- 6. Nosei L, Avalos M, Gómez BJ, Nachez L and Feugeas J. Stability under temperature of expanded austenite developed on stainless steel AISI 316L by ion nitriding. Thin Solid Films 2004; 468:134-141. http://dx.doi.org/10.1016/j.tsf.2004.06.094
- 7. Olzon-Dionysio M, De Souza SD, Basso RLO and De Souza S. Application of Mössbauer spectroscopy to the study of corrosion resistance in NaCl solution of plasma nitrided AISI 316L stainless steel. Surface and Coatings Technology 2008; 202:3607-3614. http://dx.doi.org/10.1016/j.surfcoat.2007.12.040
- 8. Nosei L, Farina S, Ávalos M, Náchez L, Gómez BJ and Feugeas J. Corrosion behavior of ion nitrided AISI 316L stainless steel. Thin Solid Films 2008; 516:1044-1050. http://dx.doi.org/10.1016/j.tsf.2007.08.072
- 9. Kuczynska-Wydorska M and Flis J. Corrosion and passivation of low-temperature nitrided AISI 304L and 316L stainless steels in acidiďŹed sodium sulphate solution. Corrosion Science 2008; 50:523-533. http://dx.doi.org/10.1016/j.corsci.2007.07.003
- 10. Gontijo LC, Machado R, Kuri SE, Casteletti LC and Nascente PAP. Corrosion resistance of the layers formed on the surface of plasma-nitrided AISI 304L steel. Thin Solid Films 2006; 515:1093-1096. http://dx.doi.org/10.1016/j.tsf.2006.07.075
- 11. Borgioli F, Fossati A, Galvanetto E, Bacci T and Pradelli G. Glow-discharge nitriding of AISI 316L austenitic stainless steel: influence of treatment time. Surface and Coatings Technology 2006; 200:3511-5513. http://dx.doi.org/10.1016/j.surfcoat.2005.07.073
- 12. Fossati A, Borgioli F, Galvanetto E and Bacci T. Glow-discharge nitriding of AISI 316L austenitic stainless steel: influence of treatment temperature. Surface and Coatings Technology 2005; 200:2474-2480. http://dx.doi.org/10.1016/j.surfcoat.2004.07.110
- 13. Franco AR Jr, Pintaúde G, Sinatora A, Pinedo CE and Tschiptschin AP. The Use of a Vickers Indenter in Depth Sensing Indentation for Measuring Elastic Modulus and Vickers Hardness. Materials Research 2004; 7:483-491. http://dx.doi.org/10.1590/S1516-14392004000300018
- 14 International Organization for Standardization - ISO. ISO 10993-5: Biological testing of medical and dental materials devices-part 5: tests for cytotoxicity: in vitro methods. Switzerland; 2009.
- 15. Rodas ACD, Maizato MJS, Leiner AA, Pitombo RNM, Polakiewicz B, Beppu MM et al. Cytotoxicity and Genotoxicity of Bovine Pericardium Preserved in Glycerol. Artificial Organs 2008; 32:272-276. http://dx.doi.org/10.1111/j.1525-1594.2008.00542.x
- 16. Wang L, Xu X, Yu Z and Hei Z. Low pressure plasma arc source ion nitriding of Austenitic stainless steel. Surface and Coatings Technology 2000; 124:93-96. http://dx.doi.org/10.1016/S0257-8972(99)00637-4
- 17. Liu MX, Ma F, Huang P, Zhang JM and Xu KW. Scale dependent plastic deformation of nanomultilayers with competitive effects of interphase boundary and grain boundary. Materials Science and Engineering: A. 2008; 477:295-299. http://dx.doi.org/10.1016/j.msea.2007.05.040
- 18. Blawert C, Kalvelage H, Mordike BL, Collins GA, Short KT, Jirásková Y et al. Nitrogen and carbon expanded austenite produced by PI3 Surface and Coatings Technology 2001; 136:181-187. http://dx.doi.org/10.1016/S0257-8972(00)01050-1
- 19. Templier C, Stinville JC, Villechaise P, Renault PO, Abrasonis G, Rivière JP et al. On lattice plane rotation and crystallographic structure of the expanded austenite in plasma nitride AISI 316L steel. Surface and Coatings Technology 2010; 204:2551-2558. http://dx.doi.org/10.1016/j.surfcoat.2010.01.041