Pinos de fibra de vidro pós tratamento - influencia a resistência de união do cimento resinoso?

BORGES, Marciano de Freitas; TEIXEIRA, Gabriela Simões; MONTAGNER, Anelise Fernandes; SUSIN, Alexandre Henrique

Acessibilidade / Reportar erro

Brasil

Revista de Odontologia da UNESP

Español English

Brasil

Español English

sumário « anterior atual seguinte »

Sumário

Original Article • Rev. Odontol. UNESP 48 • 2019 • https://doi.org/10.1590/1807-2577.03219 copiar

Pinos de fibra de vidro pós tratamento - influencia a resistência de união do cimento resinoso?

Autoria SCIMAGO INSTITUTIONS RANKINGS

Resumo

Introdução

Pinos de fibra de vidro são utilizados para melhorar a retenção das restaurações em dentes tratados endodonticamente.

Objetivo

Avaliar a resistência de união de pinos de fibra de vidro submetidos a diferentes tratamentos superficiais e cimentados à dentina radicular com cimento resinoso autoadesivo.

Material e método

trinta raízes de caninos humanos foram preparadas e divididas de acordo com dois fatores: tratamentos de superfície (silano, peróxido de hidrogênio a 35% ou bicarbonato de sódio) e o terço radicular (cervical e médio). Os pinos de fibra de vidro foram cimentados com cimento resinoso autoadesivo (RelyX U200) e foram divididos de acordo com duas regiões: cervical e terço médio. Após 24 horas, foram preparados para microtração (formato de ampulheta), padrão de fratura e avaliação micromorfológica por microscopia eletrônica de varredura, para medir a linha de cimento.

Resultado

Os dados (MPa e µm) foram submetidos à ANOVA two-way e teste de Tukey (α = 5%). Os tratamentos de superfície influenciaram a resistência de união dos pinos. A média da resistência de união (desvio padrão) diferiu de acordo com a região da dentina radicular (p <0,00): a região cervical (Controle: 19,16Mpa (3.71); Silano: 25,65MPa (4.04); Peróxido de hidrogênio: 24,43MPa (3.16); Bicarbonato de sódio: 37,42MPa (8.27)) apresentou valores de resistência a raiz (Controle: 14,66MPa (4.65); Silano: 12,52MPa (5.03); peróxido de hidrogênio: 10,64MPa (3.33); bicarbonato de sódio: 10,87MPa (2.49)).

Conclusão

O tratamento com agentes químicos e físicos aumentou a resistência de união da interface cimento-pino-dentina no terço cervical e o tratamento com bicarbonato de sódio apresentou melhores resultados na resistência de união.

Descritores:
Cimento resinoso; pino de fibra; tratamento de superfície; adesão; dentina

Materials	Product	Manufacturer	Batch no.
Glass-Fiber Post	Exacto #1	Angelus, Londrina, PR, Brazil	38064
Resin Cement	RelyX U200^* * Also available as RelyXUnicem 2.	3M ESPE, Germany	1402400622
35% Hydrogen Peroxide	Whiteness HP	FGM, Joinville, SC, Brazil	25814
Silane	Silane	Angelus, Londrina, PR, Brazil	36339
Sodium Bicarbonate	Sodium Bicarbonate	Polident, Cotia, SP, Brazil	46482

Groups (6)	Treatment of the surface of the glass fiber post	U200 - Fiber glass post cementation
Control (C)	Clean the post surface by agitation with 70% alcohol. Dry with compressed ai	1. The post and the root were prepared according to the test conditions. 2. The root was rinsing with water; 3. The excess of moisture was dry with absorbent paper; 4. the resin cement was proportioned and mixed; 5. a Centrix syringe with metal cannula was used to insert the resin cement in the prepared root until complete filling; 6. The fiber glass post was inserted vertically until the adaptation of the apical third; 7. The resin cement in excess on the cervical wall was removed with cotton; 8. Left undisturbed for 6 m; 9. Additional curing by photo-cure for 40 s
Silane (Sil)	Clean the post surface by agitation with 70% alcohol. Dry with compressed air. Apply the silane coupling agent for 60 s. Dry with compressed air.
35% Hydrogen Peroxide (Per)	Clean the post surface by agitation with 70% alcohol. Immerse in hydrogen peroxide solution for 5 min. Clean with distilled water for 60 s. Dry with compressed air. Apply the silane coupling agent for 60 s. Dry with compressed air.
Sodium Bicarbonate (Bic)	Clean the post surface by agitation with 70% alcohol. Sandblast with sodium bicarbonate for 60 s (pressure 60 to 80 PSI) with manual rotation of the post at a distance of 20 mm. Clean with distilled water for 60 s. Dry with compressed air. Apply the silane coupling agent for 60 s. Dry with compressed air.

Resin Cement

Composition

RelyX U200^* * Also available as RelyXUnicem 2.

Glass powder, surface modified with 2- propenoic acid, 2 methyl-.3-(trimethoxysilyl) propyl, bulk material
Substituted dimethacrylate
1,12-dodecane dimethycrylate
Ed dimethacrylate
2,4,6(1h,3h,5h)-pyrimidinetrione, 5-phenyl-1- (phenylmethyl)-, calcium salt (2:1)
Silane treated silica
Sodium p-2-propenoic acid, 2-methyl-, [(3- methoxypropyl)imino]di-2,1-ethanediyl ester toluenesulfinate
Calcium hydroxide
Methacrylateamine
NUC- titanium dioxide

Root Region	Group				Thickness of cement line
Root Region	Control (C)	Silane (Sil)	35% Hydrogen Peroxide (Per)	Sodium Bicarbonate (Bic)	Thickness of cement line
Cervical	19.16 (3.71) ^Ba	25.65 (4.04) ^Ba	24.43 (3.16) ^Ba	37.42 (8.27) ^Aa	762^*
Middle	14.66 (4.65) ^Aa	12.52 (5.03) ^Ab	10.64 (3.33) ^Ab	10.87 (2.49) ^Ab	414

Group	Cervical	Middle
Control (C)	Cement-dentin 25% Cement-post 50% Mixed 25%	Cement-dentin 77% Cement-post 33% Mixed 0
Silane (Sil)	Cement-dentin 25% Cement-post 40% Mixed 35%	Cement-dentin 70% Cement-post 12% Mixed 18%
Hydrogen Peroxide (Per)	Cement-dentin 43% Cement-post 24% Mixed 33%	Cement-dentin 88% Cement-post 6% Mixed 6%
Bicarbonate (Bic)	Cement-dentin 27% Cement-post 27% Mixed 46%	Cement-dentin 87% Cement-post 13% Mixed 0

Universidade Estadual Paulista Júlio de Mesquita Filho Rua Humaitá, 1680 - Caixa Postal 331, 14801-903 Araraquara,São Paulo,SP, Tel.: (55 16) 3301-6376, Fax: (55 16) 3301-6433 - Araraquara - SP - Brazil
E-mail: adriana@foar.unesp.br

Acompanhe os números deste periódico no seu leitor de RSS

[1] CONFLICTS OF INTERESTS The authors declare no conflicts of interest.